Description
BCCX-TGWJ3 is based on polyolefin, the special flame retardant is mixed by special process, after mixing the catalyst masterbatch (mass ratio 25:5). It is extruded and formed by single -screw extruder, it can be used for solar cable sheath. Cross-linking by warm water or under nature conditions (depending on the climate). The customer decides according to the actual situation. This grade is compliant to EN 50618 and passed all properties.
Standard
JB/T10436-2004
GB／T19666-2005
Specification
| Properties | Units | Typcal Value | Test Method |
|---|---|---|---|
|
Density |
g/cm3 |
1.48 |
ASTM D-792 |
|
Tensile Strength Before Crosslinking |
Mpa |
11.5 |
IEC60811-1-1 |
|
Elongation Before crosslinking |
% |
200 |
IEC60811-1-1 |
|
Tensile Strength After Crosslinking |
Mpa |
12.5 |
IEC60811-1-1 |
|
Elongation After Crosslinking |
% |
220 |
IEC60811-1-1 |
|
After Aging Condition |
℃ |
158±2*168h |
IEC60811-1-1 |
|
Retention of tensile strength |
% |
10 |
|
|
Retention of E |
% |
-16 |
|
|
Dielectric Strength |
MV/m |
32 |
IEC60520 |
|
Low temperature Impact Brittle Property |
℃ |
-40 |
IEC60811-1-4 |
|
20℃ Volume Resistivity |
Ω·-cm |
≥1.0×1012 |
IEC60167 |
|
Oxygen Index |
% |
≥30 |
ISO4589-2 |
|
Hot Set 200℃ and 0.2Mpa for 15min |
Elongation at Load |
45 |
IEC60811-2-1 |
|
|
Permanent Deformation after Cooling |
|
|
|
Smoke Density |
-flame |
50 |
ASTM E-662 |
|
|
-non-flame |
210 |
|
|
Halogen Acid Gas Content |
Mg/g |
≤5 |
IEC50267-2-1 |
|
Electrical Conductivity |
Us/mm |
0.5 |
IEC50267-2-2 |
|
Toxicity Index |
|
1 |
NES713 |
Process Techniques
Extruding techniques
The recommended setting temperatures for each zone of the extruder are as follows:
| Neck | Compress on Zone | Metering Zone | Extruder Head | Die | Max. Melt Temperature |
|---|---|---|---|---|---|
|
110℃±5℃ |
120℃± 5℃ |
130℃±5 ℃ |
140℃± 5℃ |
140℃ ±5℃ |
150℃ |
Using
(1) The product consists of two parts: a silane crosslink halogen-free low smoke flame retardant polyolefin cable material (material A)/25kgs, and a catalyst masterbatch (material B)/5kgs. Mix the two with ratio of 25:5 when used.
(2) Ensure the catalyst master batch is evenly dispersed in the material A to prevent the partial amount of catalyst too large or too small. It affects the crosslinking quality. If you need to add the color masterbatch, mix the dry color masterbatch evenly.
(3) Arrange the material before line of working, the surface of the melt is smooth and delicate, and it can be stretched to go online, As the surface of the melt is rough, the extrusion temperature can be properly reduced, the temperature of the melt is controlled at around 145 degrees, too high temperature can cause pre-crosslinking of materials and get point, too low may cause poor plasticization.
(4) Package breakage is strictly prohibited, if the remaining material are not used in the process of use, the package is sealed immediately. It should not be exposed to the air for a long time and used in 8 hours. otherwise the material should be scrapped. If any component is found to be damaged or leaked, it is strictly forbidden to mix.
(5) As far as possible, the residence time of the material in the barrel can be shortened. If the residence time is long, the material will be discharged before the surface is smooth.
(6) If you add color masterbatch, you can choose our special color masterbatch, or use color masterbatch after drying and mix evenly.
(7) Ensure the equipment cooling system is normal and effective.
(8) The material is quite sensitive to moisture and temperature, so the package is moisture-proof, customers don’t need to pre-dry the material, open the package mix can be used.
Packing, Storage & Transport
| Packing | A material: 25kgs/bag, B material: 5kgs/bag |
|---|---|
|
Transport requirement |
Keep away from the sunshine, rain and soaking during transport, as well as handle gently during carrying. |
|
Storage Environment |
Clean, dry and ventilated warehouses. |
|
To be used |
Within 6 months upon manufacturing date |